Název:	Preparation of magnetic bentonite
Citace	Mucha, M. Preparation of magnetic bentonite. In: Nano Ostrava 2013 - 3rd Nanomaterials and Nanotechnology Meeting. Ostrava: VŠB-TU Ostrava, 2013. VŠB-TU Ostrava, 2013. s. 112-112. ISBN 978-80-7329-361-1.

Podnázev
Rok vydání:	2013
Obor:	Kompositní materiály
Počet stran:	1
Strana od:	112
Strana do:	112
Forma vydání:	Tištená verze
Kód ISBN:	978-80-7329-361-1
Kód ISSN:
Název sborníku:	Nano Ostrava 2013 - 3rd Nanomaterials and Nanotechnology Meeting
Sborník:	Mezinárodní
Název nakladatele:	VŠB-TU Ostrava
Místo vydání:	Ostrava
Stát vydání:	Sborník vydaný v ČR
Název konference:	Nano Ostrava 2013
Místo konání konference:	Ostrava
Datum zahájení konference:
Typ akce podle státní příslušnosti účastníků akce:	Celosvětová akce
Kód UT WoS:
EID:

Klíčová slova anglicky:	bantonite, magnetite, magnetic materials, composite materials, sorbents
Popis v původním jazyce:	This work deals with preparation and characterization of composite magnetic materials based on bentonite. Materials were prepared by co-precipitation method with magnetite/maghemite particles formation. Two ratios of Fe(III) and Fe(II) (1:1 and 2:1) were used. Magnetic properties and FTIR specta were measured. Materials prepared with 1:1 ratio exhibit better magnetic properties than materials prepared with Fe(III) and Fe(II) ratio 2:1.
Popis v anglickém jazyce:	This work deals with preparation and characterization of composite magnetic materials based on bentonite. Materials were prepared by co-precipitation method with magnetite/maghemite particles formation. Two ratios of Fe(III) and Fe(II) (1:1 and 2:1) were used. Magnetic properties and FTIR specta were measured. Materials prepared with 1:1 ratio exhibit better magnetic properties than materials prepared with Fe(III) and Fe(II) ratio 2:1.